Formation Process of Long-Period Stacking-Ordered Structures in Mg97Zn1Y2 Alloy Comprising HCP and Cubic Phases Fabricated by High-Pressure High-Temperature Annealing

As-cast Mg97Zn1Y2 alloy consists of α-Mg matrix and 18R-type long-period stacking-ordered (LPSO) structures. We observed that the alloy undergoes a phase transformation to D03 superlattices and α-Mg matrix due to high-pressure high-temperature (HPHT) annealing at 3 GPa and above 773 K. Further, the...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Metals (Basel ) 2021-07, Vol.11 (7), p.1031
Hauptverfasser: Yokota, Atsuki, Matsushita, Masafumi, Geshi, Naruhito, Yamasaki, Daiki, Shinmei, Toru, Yamasaki, Michiaki, Kawamura, Yoshihito
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:As-cast Mg97Zn1Y2 alloy consists of α-Mg matrix and 18R-type long-period stacking-ordered (LPSO) structures. We observed that the alloy undergoes a phase transformation to D03 superlattices and α-Mg matrix due to high-pressure high-temperature (HPHT) annealing at 3 GPa and above 773 K. Further, the alloy recovered after HPHT annealing, consisting of the α-Mg matrix and D03 superlattices, transformed into 18R-type LPSO structures during further annealing at ambient pressure. An fcc structure with a lattice parameter of 1.42 nm, which was twice that of D03, emerged in both the collapse process of the 18R-type LPSO structure under high-pressure, and the formation process of the 18R-type LPSO structure at ambient pressure. This fcc phase was an intermediate structure between 18R-type LPSO and D03. From the electron diffraction results, it is considered that 18R-type LPSO is continuously present with 2H including stacking faults, which almost corresponded with previous studies.
ISSN:2075-4701
2075-4701
DOI:10.3390/met11071031