Tensile Strength, Micro-hardness and Microstructure of Friction-Stir-Welding AA6061-T4 Joints

Welding of aluminum alloys by traditional welding methods creates some defects such as hot cracks, porosity, and void that led to decreasing of mechanical properties. Friction Stir Welding (FSW) gives good mechanical properties of aluminum alloy welds. In this paper, FSW worked in 4 mm thick plate o...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Tikrit journal of engineering sciences 2018-12, Vol.25 (4)
Hauptverfasser: Najeeb S. Abtan, Ataalah Hussain Jassim, Mustafa S. M. Al-Janabi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Welding of aluminum alloys by traditional welding methods creates some defects such as hot cracks, porosity, and void that led to decreasing of mechanical properties. Friction Stir Welding (FSW) gives good mechanical properties of aluminum alloy welds. In this paper, FSW worked in 4 mm thick plate of 6061-T4 aluminum alloy, with two welding parameters are used (tool rotational speed and feed rate) was investigated, were analyzed the microstructure and mechanical properties by carried out microstructural, micro-hardness, and tensile strength tests. From results are found defect-free of welds at a wide range of parameters. Stir zone shows a fine-equiaxed grain and high hardness, not significantly change between heat affected zone and base metal in size grain. Tensile strength of welds was lower than base metal and fracture location was occurred at a low hardness region for the welds.
ISSN:1813-162X
2312-7589