Abnormal mechanical property evolution induced by heat treatment for a semi-solid forming hypereutectic Al-Fe base alloy

In the present study, Al-5.5Fe-4Cu-2Zn-0.4Mg-0.5Mn al oy samples were prepared by electromagnetic stirring and semi-solid forming processing, and then the effects of T6 and T1 heat treatments on the microstructures and mechanical properties of the semi-solid forming samples were investigated. The results indicate that after semi-solid forming, the mechanical properties of the sample improved significantly compared to that of the merely electromagnetically stirred sample. The grains of semi-solid forming alloy became almost fine equiaxed; big long strip-shaped Al3 Fe phases became short rod-like morphology and distributed uniformly in the matrix. However, the mechanical properties of the T6-treated semi-solid forming sample decreased significantly instead of increasing and, with solution temperature rising, the tensile strength of the al oy decreased further. The results of EDS show that after high temperature solid-solution treatment, the Cu element in the semi-solid forming alloy sample is mainly concentrated at the boundaries of the Al3 Fe phases instead of being dissolved in the matrix. At the same time, the grains of the semi-solid forming sample grew slightly after solid-solution treatment. Therefore, the growth of the grains and the accumulation of Cu element at Al3 Fe phase boundaries during solution treatment of the semi-solid forming alloy were the main reasons for the mechanical properties decreasing after T6 treatment. The mechanical properties of the alloy were improved after T1 heat treatment due to aging strengthening phase being precipitated in the matrix.