In-situ Investigation of the Fracture Behaviors of 2195-T8 Aluminum-Lithium alloy

In this paper, the tensile crack initiation and propagation behavior of 2195-T8 Aluminum-Lithium alloy was studied by in situ scanning electron microscope observation at room temperature. It was found that cracks initiated at second phases which propagated along the grain boundaries only as T1 phases could retard crack growth inside grains. With further increase of strain, within the grain a large number of slip bands were produced, resulting in the deflection of the grains, which leaded to transgranular fracture at last. SEM examination show both intergranular and transgranular fracture surface morphology indicating that the 2195-T8 alloy revealed a mix mechanism for the fracture.