Microstructure and mechanical properties of Al2O3/AZ31 composites prepared by multi-pass hot extrusion

Multi-pass hot extrusion was used to prepare the Al2O3/AZ31 composite.The microstru-cture was characterized by optical microscopy, scanning electron microscopy, transmission electron microscopy, and mechanical properties were tested by Vickers hardness tester and electron universal strength tester. The results show that Al2O3 particles are uniformly distributed in AZ31 magnesium matrix by multi-pass hot extrusion. The grain refining effect of Al2O3 particles on the matrix is enhanced, and the grain size of the composite decreases significantly with the increase of the pass. During the hot extrusion process, the dislocation density around the Al2O3 particles increases, and the high-density dislocation region facilitates the dynamic recrystallization nucleation, so that the grains of the Al2O3/AZ31 composite are significantly refined. The Al2O3 particles are gradually distributed into a long strip from the initial island distribution, then distributed in a linear pattern, and finally distributed uniformly in th