Morphological and Crystallographic Characterization of Primary Zinc-Rich Crystals in a Ternary Sn-Zn-Bi Alloy under a High Magnetic Field

Due to the unique capacity for structural control, high magnetic fields (HMFs) have been widely applied to the solidification process of alloys. In zinc-based alloys, the primary zinc-rich crystals can be dendritic or needle-like in two dimensions. For the dendritic crystals, their growth pattern an...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Crystals (Basel) 2017-07, Vol.7 (7), p.204
Hauptverfasser: Li, Lei, Ban, Chunyan, Zhang, Ruixue, Zhang, Haitao, Cai, Minghui, Zuo, Yubo, Zhu, Qingfeng, Wang, Xiangjie, Cui, Jianzhong
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Due to the unique capacity for structural control, high magnetic fields (HMFs) have been widely applied to the solidification process of alloys. In zinc-based alloys, the primary zinc-rich crystals can be dendritic or needle-like in two dimensions. For the dendritic crystals, their growth pattern and orientation behaviors under HMFs have been investigated. However, the three-dimensional crystallographic growth pattern and the orientation behaviors of the needle-like primary zinc-rich crystals under a high magnetic field have not been studied. In this work, a ternary Sn-Zn-Bi alloy was solidified under different HMFs. The above-mentioned two aspects of the needle-like primary zinc-rich crystals were characterized using the Electron Backscattered Diffraction (EBSD) technique. The results show that the primary zinc-rich crystals are characterized by the plate-shaped faceted growth in three dimensions. They grow in the following manner: spreading rapidly in the {0001} basal plane with a gradual decrease in thickness at the edges. The application of HMFs has no effect on the growth form of the primary zinc-rich crystals, but induces their vertical alignment. Crystallographic analysis indicates that the vertically aligned primary zinc-rich crystals orient preferentially with the c-axis perpendicular to the direction of the magnetic field.