Fabrication of Hybrid Epoxy Composites (Joint Compound Adhesive) for Aluminum Substrate Applications and Their Evaluation for Mechanical Properties

This research endeavor deals with the development of an epoxy hybrid nanocomposite using aliphatic diglycidyl ether of a bisphenol A (DGEBA) epoxy matrix. The formulation used the stoichiometric ratio of the curing agent and incorporated nanopigments such as zirconium and silica, along with other microfillers. We incorporated Zr and SiO2 nanoparticles and various other additives in the epoxy matrix and ensured homogeneous dispersion by using sonication methodology along with silane as a coupling agent. Aluminum molds were utilized to fabricate dumbbell-shaped ASTM standard samples for the testing of mechanical properties. The adhesive properties were evaluated through standard lap shear tests. Fourier transform infrared spectroscopy was utilized to analyze the cross-linking reaction of the epoxy moiety and the polyamidoamine adduct curing agent. Further characterization using field emission scanning electron microscopy, energy-dispersive spectroscopy, and high-resolution transmission electron microscopy confirmed the presence and uniform dispersion of the fillers and nanopigments. The results showed good enhancements in ultimate tensile strength, yield strength, and elastic modulus of 95.3, 162.1, and 425.4%, respectively, compared to formulations using only SiO2. The addition of ZrO2 and SiO2, along with various microfillers, such as talc and aluminum silicate, led to significant improvements in the mechanical properties. This study demonstrates the synergistic efficiency of combining SiO2 and ZrO2 along with microfillers, such as talc and aluminum silicate, in epoxy resin for diverse applications in the construction industry, where mechanical strength and substrate adhesion are crucial.