Structure and properties of solid solutions in the Mg-Al-B system

Compounds with the general formula Mg 1− x Al x B 2 were obtained by two-step ceramic synthesis. All compounds were characterized by X-ray diffraction, NMR spectroscopy, and by four point probe resistivity measurements in various magnetic fields method. The diborides unit cell parameters were determined as a function of the Al mole fraction. With the vaues of x up to 0.40 (where x is the composition of the stock prepared for sintering), the unit cell parameters of Mg 1− x Al x B 2 are similar to those of pure MgB 2 and the superconducting transition temperature was lowered. For stock compositions of 0:25 ≤ x ≤ 0:60, the products contain a superstructure, also superconducting phase, which becomes the only product at x = 0:50, and at x > 0:60 this phase is replaced by AlB 2 -based solid solutions.