Assessment of aging effects on porcelain repair systems discoloration
Introduction: The selection of porcelain is based on high biocompatibility, endurance, superficial texture and aesthetics. Nevertheless, the innate fracture charateritics of porcelain is the main cause of the intra oral fractures. Electing a suitable porcelain restorative system in terms of stabilit...
Gespeichert in:
Veröffentlicht in: | Caspian journal of dental research 2013-03, Vol.2 (1), p.46-52 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Introduction: The selection of porcelain is based on high biocompatibility, endurance, superficial texture and aesthetics. Nevertheless, the innate fracture charateritics of porcelain is the main cause of the intra oral fractures. Electing a suitable porcelain restorative system in terms of stability of color is important. For this reason, this study aimed to examine the color changes of common porcelain repair materials. Methods: Using a silicon mold, 30 pieces of feldspathic porcelain in A3 color, 10mm of diameter and 2 mm of thickness were prepared. The samples were randomly distributed into three groups: Group 1: Porcelain-Silane-Bonding-Composite Group 2: Porcelain-Silane-Bonding-Panavia F 2.0-Bonding-Silane-Porcelain Group 3: Porcelain-Silane-Bonding-Choice 2 -Bonding-Silane-Porcelain The aging process was accomplished with thermocyling (3000 cycles, 5/55 degree), incubation in 37° and 100° humidity. Thereafter, discoloration was assessed In CIE system via designation of color transforming matrix in MATLAB environment . Results: The average quantitative amount of discoloration at day 0, 90 and 180 were 76.8±0.57, 79.15±0.52, 80.13±0.6 for Choice, 78.03±0.9, 79.42±0.82, 80.17±0.51 for Panavia, and 78.41±1.53, 79.59±0.77, 81.03±0.63 for Composite, respectively. The color changes by the time were significant for the all three groups (p |
---|---|
ISSN: | 2251-9890 2322-2395 |