Preparation and Property Study of PA56/POE-g-MAH-GMA/PPO Ternary Alloy

Bio-based PA56 is as matrix resin, maleic anhydride (MAH), and glycidyl methacrylate (GMA) dual monomer grafted POE (POE-g-MAH/GMA) polyphenyl ether(PPO) are simultaneous as toughening agents. The PA56/POE-g-MAH-GMA/PPO ternary alloys containing 10 wt% POE-g-MAH-GMA with different PPO content prepared by the melt blending method through twin screw extruder. The structure and property of PA56/POE-g-MAH-GMA/PPO ternary alloys were studied. The results showed that the microscopic morphology of each alloy showed an obvious “sea-island” structure. PA56 is a continuous sea phase, and the island phase assumes the “core–shell structure,” the etched POE-g-MAH-GMA particles are as the nucleus, and PPO are as the shell. When the PPO mass fraction is 30%, the relative crystallinity of the alloy is 11.56%, which is 1.68 times lower compared to the pure PA56, the alloy notch impact strength is 42.1 kJ/m2, and reaches 11.7 times of pure PA56; the water absorption rate of 1.22%, which is 3.22 times lower than pure PA56.