Carbon Nanotube and Cellulose Nanocrystal Hybrid Films

The use of cellulose nanocrystals (CNC) in high performance coatings is attractive for micro-scale structures or device fabrication due to the anisotropic geometry, however CNC are insulating materials. Carbon nanotubes (CNT) are also rod-shaped nanomaterials that display high mechanical strength an...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Molecules (Basel, Switzerland) Switzerland), 2019-07, Vol.24 (14), p.2662
Hauptverfasser: Jiang, Mingzhe, Seney, Robert, Bayliss, Paul Charles, Kitchens, Christopher L
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The use of cellulose nanocrystals (CNC) in high performance coatings is attractive for micro-scale structures or device fabrication due to the anisotropic geometry, however CNC are insulating materials. Carbon nanotubes (CNT) are also rod-shaped nanomaterials that display high mechanical strength and electrical conductivity. The hydrophobic regions of surface-modified CNC can interact with hydrophobic CNT and aid in association between the two anisotropic nanomaterials. The long-range electrostatic repulsion of CNC plays a role in forming a stable CNT and CNC mixture dispersion in water, which is integral to forming a uniform hybrid film. At concentrations favorable for film formation, the multiwalled nanotubes + CNC mixture dispersion shows cellular network formation, indicating local phase separation, while the single-walled nanotube + CNC mixture dispersion shows schlieren texture, indicating liquid crystal mixture formation. Conductive CNT + CNC hybrid films (5-20 μm thick) were cast on glass microscope slides with and without shear by blade coating. The CNT + CNC hybrid films electrical conductivity increased with increasing CNT loadings and some anisotropy was observed with the sheared hybrid films, although to a lesser extent than what was anticipated. Percolation models were applied to model the hybrid film conductivity and correlate with the hybrid film microstructure.
ISSN:1420-3049
1420-3049
DOI:10.3390/molecules24142662