Effect of Na2O/SiO2 mole ratio on the crystal type of zeolite synthesized from coal fly ash

Effect of Na2O/SiO2 mole ratio on the crystal type of zeolite synthesized from coal fly ash

Coal fly ash was modified to zeolitic materials by hydrothermal treatment at 90ºC. The zeolite synthesis was studied as a function of the mole ratio of Na2O/SiO2 in the reaction mixtures. The results showed that NaP1 zeolite is obtained when the Na2O/SiO2 mole ratio was 0.7. Hydroxysodalite is the d...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of the Serbian Chemical Society 2003-06, Vol.68 (6), p.471-478
Hauptverfasser: PREDRAG LAZIC, ALEKSANDRA ROSIC, IGOR MILJANOVIC, DUSICA VUCINIC
Format: Artikel
Sprache:eng
Schlagworte:
coal fly ash
hydrothermal treatment
zeolitic materials
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Coal fly ash was modified to zeolitic materials by hydrothermal treatment at 90ºC. The zeolite synthesis was studied as a function of the mole ratio of Na2O/SiO2 in the reaction mixtures. The results showed that NaP1 zeolite is obtained when the Na2O/SiO2 mole ratio was 0.7. Hydroxysodalite is the dominant zeolite phase in modified fly ash treated with a higher Na2O concentration solution (Na2O/SiO2 = 1.3). The IR and XRD methods were used to determine the phases present in the starting sample and in the zeolitic materials.
ISSN:0352-5139