Evaluation of Biomass Solid Waste as Raw Material for Preparation of Asphalt Mixture

At present, the resource utilization of solid waste in China is facing prominent problems such as high production intensity, insufficient utilization, and low added value of products. The preparation of biomass composites from biomass solid waste and plastic solid waste reduces not only environmental pollution and energy consumption but also promotes the high-value utilization of solid waste. So, the characterization and preparation experiments of samples with two different biomass are carried out. The wheat straw fiber and corn straw fiber were added into the bio-asphalt mixture with the content of 0.1%, 0.2%, 0.3%, and 0.4%, respectively, with the content of 9% and 12% bio-heavy oil. The physical properties and rheological properties of asphalt were analyzed and evaluated by three indexes and a dynamic shear rheological test. Through the rutting test and immersion Marshall test, high-temperature performance and biological asphalt mixture’s water stability were evaluated. The results show that straw fiber can improve bio-asphalt mixture’s road performance, especially the performance of high-temperature rutting. When the fiber content of bio-asphalt with 9% bio-heavy oil content is 0.3%, the physical properties and rheological properties of bio-asphalt are the best. Corn straw fiber’s influence on bio-asphalt mixture was better than that of wheat straw fiber.