The Forecasting of Corrosion Damage of Structural Materials during Dry Long-Term Storage of RD BN-350 SNF with CC-19 SFA

There are results of long-term thermal aging of samples of irradiated and nonirradiated FA jacket and nonirradiated fuel element cladding at a temperature range from 300 to 550°C in argon, to 600°C in air. Materials have been studied before and after thermal tests. The forecast estimation of expected corrosion damage of barrier material at the radionuclide release from spent fuel assemblies of BN-350 reactor into environment during dry storage for 50 years was carried out.