Chemical Species Formed on FeB-Fe2B Layers during Wet Sliding Wear Test

In the present work, X-ray photoelectron spectroscopy (XPS) survey spectra of borided AISI 316L for two different times (1 and 6 h) of exposure to simulated body fluid (SBF) were obtained after wet sliding wear. A borided layer of ~39 microns was obtained on the surface of the AISI 316L stainless steel using the thermochemical treatment of boriding. As part of the mechanical and chemical characterization of sliding wear, Berkovich nanoindentation and X-ray spectroscopy tests were used to determine the main properties of the borided layer. The results of the specific wear rate values were higher at 5 mm/s sliding speed than those recorded at 30 mm/s due to the influence of the exposure time of the sample and the complex combinations of chemical reactions with boron (e.g., B2S3, Cr2O3, and Fe2O3) on the surface during the sliding during 6 h of exposure in Hank’s solution due to the formation of the passive film. The knowledge of chemical species formed during wet sliding wear tests on borided AISI 316L is essential for understanding wear mechanisms and materials’ performance and optimizing material properties and materials’ and components’ reliability in the biomedical industry for screws and fastening plates.