Comparison of shear bond strength of composite resin, compomer, and resin-modified glass-ionomer cements in primary teeth: An in-vitro study

OBJECTIVE: The contemporary esthetic restorative materials such as composite resin and glass-ionomer cements and their modifications have all been developed keeping in mind the requirements of permanent teeth. There have been plenty of studies that have focused on the characteristics of these materials in relation to permanent teeth with a relative dearth of such studies as regard to the primary teeth. The present study was undertaken to compare and evaluate the shear bond strength of composite resin, compomer, and resin-modified glass-ionomer cements in primary teeth. METHODS: Thirty non-carious primary molars that were indicated for extraction because of physiological resorption or, for orthodontic reasons, were selected. The selected teeth were randomly allocated to three groups of 10 each for composite, compomer, and resin-modified glass-ionomer cements. The enamel from the occlusal surface of all teeth was removed to expose the superficial dentin and was wet polished with 400 grit sand paper. Composite, compomer, and resin-modified glass-ionomer stubs were bonded on to the occlusal surfaces using a plastic tube as a template. All samples were, then, subjected to thermocycling and evaluation of shear bond strength using the universal testing machine at a cross-head speed of 0.5 mm/min, whereas the results obtained were subjected to statistical analysis. Statistical analysis was performed using Statistical Package for Social Sciences (SPSS) version 17.0 (SPSS Inc., Chicago, IL, USA), whereas one-way analysis of variance (ANOVA) and Tukey's multiple post-hoc procedures were used for statistical analysis. A P < 0.05 was considered statistically significant. RESULTS: The mean shear bond strength values for Groups I, II, and III were found to be 11.7 ± 3.07 MPa, 7.74 ± 4.16 Mpa, and 4.43 ± 2.08 Mpa, respectively, whereas one-way ANOVA and Tukey's multiple post-hoc procedures indicated that there were remarkable differences among the three groups with the results being statistically significant (P < 0.05). CONCLUSIONS: Composite resin showed the highest shear bond strength in relation to primary dentin when compared to compomer and resin-modified glass-ionomer cements.