Synthesis and Electrochemical Characterisation of Magnetite Coatings on Ti6Al4V-ELI

Titanium alloys have been widely employed in implant materials owing to their biocompatibility. The primary limitation of these materials is their poor performance in applications involving surfaces in mutual contact and under load or relative motion because of their low wear resistance. The aim of...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Metals (Basel ) 2020-12, Vol.10 (12), p.1640
Hauptverfasser: Montiel, Adriana, Bustamante, Edgar Onofre, Escudero, María Lorenza
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Titanium alloys have been widely employed in implant materials owing to their biocompatibility. The primary limitation of these materials is their poor performance in applications involving surfaces in mutual contact and under load or relative motion because of their low wear resistance. The aim of this work is to synthesis magnetite coatings on the Ti6Al4V-ELI alloy surface to increase corrosion resistance and to evaluate its electrochemical behaviour. The coatings were obtained using potentiostatic pulse-assisted coprecipitation (PP-CP) on a Ti6Al4V-ELI substrate. The preliminary X-Ray Diffraction (XRD) results indicate the presence of the magnetite coating with 8–10 nm crystal sizes, determined for the (311) plane. Using X-ray photoelectron spectroscopy (XPS), the presence of the magnetite phase on the titanium alloy was observed. Magnetite coating was homogeneous over the full surface and increased the roughness with respect to the substrate. For the corrosion potential behaviour, the Ti6Al4V-ELI showed a modified Ecorr that was less active from the presence of the magnetite coating, and the impedance values were higher than the reference samples without coating. From the polarization curves, the current density of the sample with magnetite was smaller than of bare titanium.
ISSN:2075-4701
2075-4701
DOI:10.3390/met10121640