Phase-Field Simulation of Spinodal Decomposition in Mn-Cu Alloys

The spinodal decomposition was studied in the aged Mn-40 at. %Cu, Mn-30 at. %Cu, Mn-20 at. %Cu alloys using a phase-field model based on the Cahn–Hillard equation, considering a subregular solution model and the energy contribution of the magnetic behavior. The simulations were performed at aging te...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Metals (Basel ) 2022-07, Vol.12 (7), p.1220
Hauptverfasser: Sigala-García, Darío A., López-Hirata, Víctor M., Saucedo-Muñoz, Maribel L., Dorantes-Rosales, Héctor J., Villegas-Cárdenas, José D.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The spinodal decomposition was studied in the aged Mn-40 at. %Cu, Mn-30 at. %Cu, Mn-20 at. %Cu alloys using a phase-field model based on the Cahn–Hillard equation, considering a subregular solution model and the energy contribution of the magnetic behavior. The simulations were performed at aging temperatures of 300, 400, and 500 °C for times from 1 to 240 min. The growth kinetics of the Mn concentration profiles with time indicated clearly that the phase decomposition of the supersaturated solid solution γ into a mixture of Mn-rich γ′ and Cu-rich γ phases occurred by the spinodal decomposition mechanism. Moreover, the phase decomposition at the early stages of aging exhibited the characteristic morphology of spinodal decomposition, an interconnected and percolated microstructure of the decomposed phases. The most rapid growth kinetics of spinodal decomposition occurred for the aging of Mn-20 and 30 at. %Cu alloys because of the higher driving force. The presence of the phase decomposition is responsible for the increase in hardness, as well as the improvement of the damping capacity of Mn-Cu alloys.
ISSN:2075-4701
2075-4701
DOI:10.3390/met12071220