Synthesis of prodrug polymer as ring opening of PVP

In this work a new drug polymer was prepared from reaction of polyvinylpyrrolidone (PVP) with doxycylin in 10 : 1 dioxane : dimethelyformad solvent mixture. The prepared drug polymer was formed with 85 % conversion percentage. The physical properties were studied and intrinsic viscosity was equal to 0.23 dl / g. The drug polymer was characterized by FT-IR and UV spectroscopy. The swelling % was studied in different non solvents. The elemental analysis and DSC were analyzed. The controlled release rates for drug polymer were studied in different pH values at 37oC for 4 days. The softening point of the prepared doxycyclin drug polymer was 143.4oC to 150.3oC with ΔH = -189.89 J / g في هذا البحث حضر بوليمر دوائي من تفاعل البولي فاينيل بايروليدينون مع عقار الدوكسيسايلين في مذيب الدايوكسان و الداي مثيل فورمايد بنسبة 10 : 1 فكان ناتج التحوير بنسبة 85 % درست الصفات الفيزيائية و اللزوجة الجوهرية للبوليمر و التي تساوي (0.23dl / g) و شخص البوليمر الدوائي الناتج بواسطة الأشعة تحت الحمراء و الأشعة فوق البنفسجية، و قيست نسبة الانتفاخ المئوية في اللامذيبات. و أجري التحليل الدقيق للعناصر و تم إجراء التحليل الحراري DSC. و كذلك درست سرع التحرر الدوائي من البوليمر المحضر في دوال حامضية مختلفة عند 37 م لمدة 4 أيام. و كانت درجة سيولة البوليمر تساوي : 143.4°C-150.3°C و التغير في الإنثاليبي (189.89) ميكروجول / غم.