Effect of Calcination Temperature of SiO2/TiO2 Photocatalysts on UV-VIS and VIS Removal Efficiency of Color Contaminants

This paper presents the effect of fumed silica modification and calcination temperature on the physicochemical properties of photocatalysts and their activity under the UV-VIS and VIS light range. The materials were obtained by hydrolysis of titanium tetraisopropoxide (TTIP) combined with a calcination step. The obtained nanomaterials were characterized using analytical methods such as X-ray diffraction XRD, FT-IR/DRS infrared spectroscopy, UV-Vis/DRS spectroscopy and SEM scanning electron microscopy. BET specific surface area and zeta potential were also measured. It was observed that SiO2 modification inhibited the transformation phase of anatase to rutile and the increase in crystallite size during calcination. The calcination process contributed to a change in the surface character of photocatalysts under study from positively to negatively charged. The photocatalytic activity of samples was identified by determining the methylene blue decomposition under UV-VIS and VIS light. Experimental results showed that the addition of SiO2 and the calcination process increased the photoactivity. The obtained materials showed higher activity compared to the reference samples. It was found that the degree of dye removal increased along with increased calcination temperature. The highest activity was observed for photocatalyst SiO2(11.1%)/TiO2_600.