Research on Optimization Design of Cast Process for TiAl Case Casting

The effect of the cast process procedure and pouring systems on several typical metallurgical defects for TiAl case casting was studied by numerical simulation and pouring test. The results indicated that gravity casting had much better melt-filling stability and synchronization, compared to centrif...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Metals (Basel ) 2022-11, Vol.12 (11), p.1954
Hauptverfasser: Zhu, Xiaoping, Zhu, Chunlei, Lin, Baosen, Wang, Zidong
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The effect of the cast process procedure and pouring systems on several typical metallurgical defects for TiAl case casting was studied by numerical simulation and pouring test. The results indicated that gravity casting had much better melt-filling stability and synchronization, compared to centrifugal casting. Misrun defects in the upper edge of the thin-walled outer ring could be removed by increasing the bottom cross runners, and the negative effect of the overheated zone in the thick-walled flange could be reduced by designing a suitable inner-gate structure. The crack induced by stress concentration in the transition zone brought significant challenges for TiAl case casting and the issue would be effectively resolved through structural design and process optimization.
ISSN:2075-4701
2075-4701
DOI:10.3390/met12111954