Self-Compacting Mixtures of Fair-Faced Concrete Based on GGBFS and a Multicomponent Chemical Admixture—Technological and Rheological Properties

The use of superplasticizers in a self-compacting concrete mix without the addition of a foaming agent in practice leads to a well-known problem associated with increased air entrainment and promotes the formation of harmful large bubbles, high-void content, and ununiform appearance. This paper presents research on the properties of cement paste consisting of Ordinary Portland Cement (OPC), powder based on ground granulated blast furnace slag (GBBS), and superplasticizer. The methodology of this study was the estimation of flow diameter and flow time, as well as the evaluation of the rheological characteristics. The influence of ground granulated blast furnace slag and polycarboxylate plasticizer on the flowability and viscosity of cement paste was studied. The effect of superplasticizer (SP) based on polycarboxylate esters (PCE) anti-foaming agent (AFA) based on a glycol ester and air-entraining admixture (AEA) based on an amphoteric surfactant on flowability, viscosity, rheological properties and the strength of the cement paste was evaluated. It was found that the increase of slag content in cement paste (25%) with the presence of superplasticizer (0.64%) significantly changes the flowability and viscosity. It was stated that the addition of 0.04% anti-foaming agents increases flowability (20%) and reduces viscosity (44%) of cement paste. It was stated that the addition of small dosages of glycol ester-based anti-foaming agent (0.02 and 0.04%) significantly changes the rheological properties, decreases the shear yield stress by 2.1–2.8 times, the plastic viscosity by 2.4–2.6 times and apparent viscosity 1.6–2.5 times, improves the compressive strength at the age of 1 and 7 days by 2.5 and 1.4 times, respectively. The addition of air-entraining admixture led to a decrease in the plastic viscosity by 1.2–1.4 times. It was stated that the presence of air-entraining admixture assists in increasing the apparent viscosity by 1.7–2.4 times. It was shown that the presence of complex admixtures of various origins, purposes, and mechanisms of action would assist in predicting the behavior of concrete mixtures under the conditions of the building site and reduce the consumption of polycarboxylate esters due to the enhancing plasticizing effect of anti-foaming agent and air-entraining admixture.