Tensile, Flexural, and Morphological Properties of Jute/Oil Palm Pressed Fruit Fibers Reinforced High Density Polyethylene Hybrid Composites

The incorporation of materials that were formally regarded as agricultural wastes into polymeric matrix has drawn the attention of many researchers in recent years. This research focused on reinforcing high-density polyethylene (HDPE) matrix with treated jute fiber (JF)/oil palm pressed fruit fibers...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Fibers 2021-11, Vol.9 (11), p.71
Hauptverfasser: Daramola, Oluyemi Ojo, Balogun, Oluwatosin Abiodun, Adediran, Adeolu Adesoji, Saka, Sheriff Olalekan, Oladele, Isiaka Oluwole, Akinlabi, Esther Titilayo
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The incorporation of materials that were formally regarded as agricultural wastes into polymeric matrix has drawn the attention of many researchers in recent years. This research focused on reinforcing high-density polyethylene (HDPE) matrix with treated jute fiber (JF)/oil palm pressed fruit fibers (OPPFF) at varying weight proportions. JF and OPPFF were cut to 2.5 mm length and were chemically treated thereafter with 1 M and 1.5 M sodium hydroxide solution respectively. The composites were produced using the compression molding technique. The morphological characterization of the fibers and composites for untreated and treated samples was studied with the aid of a scanning electron microscope (SEM). Tensile and flexural properties of the produced composite samples were also determined. From the result, the surface morphology of the fiber after treatment showed that there was obvious exposure of the fiber surface and removal of impurities as this influenced the microstructure of the composites and in turn the tensile and flexural properties. Hence, it was observed that 20 wt.% treated jute fiber addition shows the most significant enhancements in terms of tensile and flexural properties. The study exposed the effect of surface modification of JF/OPPF hybridization on HDPE matrix composite.
ISSN:2079-6439
2079-6439
DOI:10.3390/fib9110071