Homogeneous Pinus sp. particle boards reinforced with laminated composite materials

ABSTRACT This study aimed to evaluate the mechanical performance of laminated composite materials (fiberglass, carbon, sisal, palm fiber) in epoxy matrix as reinforcement in wood particleboards of Pinus sp. with bicomponent polyurethane resin from castor oil. Modulus of elasticity (MOE) and modulus of rupture (MOR) were investigated using a three-point bending test. Single-layered laminated plates were used to reinforce traction of specimens obtained from boards. MOE and MOR of materials developed without reinforcements exceeded limits in ABNT standards both NBR 12810-2:2002 and A208.1:199, proving therefore their feasibility. In all investigated cases, inclusion of reinforcements led to higher values for both MOE and MOR. Composites in fiberglass presented the best results. RESUMO Este trabalho objetivou avaliar o desempenho mecânico do emprego de materiais compósitos laminados (fibras de vidro; carbono; sisal; piaçava) em matriz epóxi, como reforço em painéis de partículas de madeira Pinus sp. com resina poliuretana bicomponente, derivada de óleo de mamona. Foram investigados, com o uso do ensaio de flexão estática a três pontos, o módulo de elasticidade (MOE) e o módulo de ruptura (MOR). Os compósitos laminados foram fabricados com camada única, reforçando à tração os corpos de prova obtidos dos painéis. Os resultados do MOE e do MOR dos materiais desenvolvidos sem a inclusão dos reforços superaram os limites contidos nos documentos normativos ABNT NBR 14810-2:2002 e A208.1:199, comprovando a viabilidade dos materiais elaborados. Em todos os casos investigados, a inclusão dos reforços conduziu a valores superiores, tanto para o MOE quanto para o MOR, apresentando os compósitos em fibras de vidro os melhores resultados.