Effect of Zn on Microstructure and Wear Resistance of Sn-Based Babbitt Alloy

Tin-based Babbitt alloys are a widely used bearing bushing material which have good comprehensive properties. However, problems such as high-temperature softening and insufficient bearing capacity occur during their use, so the optimization of tin-based Babbitt alloys has become a research hotspot. In this paper, ZChSnSb11-6 alloy was mainly prepared by the gravity casting method, and different amounts of Zn were added to the alloy (the mass fraction values were 0 wt.%, 0.05 wt.%, 0.1 wt.%, 0.15 wt.%, and 0.2 wt.%, respectively). Through the hardness test, the tensile test, the friction and wear test, and the microstructure observation of the prepared alloy, the influence of Zn on the organization and properties of the ZChSnSb11-6 alloy was analyzed. The results show that the size of the SnSb hard phase changed with the increasing content of Zn. The size of the hard phase of the SnSb tended to increase first and then decrease, and the number of phase particles increased first and then decreased, resulting in changes in performance. Through comparison, it was learned that the addition of Zn can effectively improve the hardness, tensile strength, yield strength, and wear resistance of the alloy, but the elongation rate was reduced. When the Zn content was 0.1 wt.%, the hardness value of the alloy reached the maximum value, 25.82 HB, which increased by 7.3% when compared with the sample without Zn. The hardness of the Zn, 0.15 wt.%, is close to that of the Zn, 0.1 wt.%. Compared to the sample without Zn, the tensile strength and elongation of the alloy were maximized at a Zn content of 0.15 wt.%. Compared to the sample without the Zn, the tensile strength was increased by 21.29%, and the elongation rate was increased by 46%. An analysis showed that the alloy has good comprehensive mechanical properties when the Zn content is 0.15 wt.%.