Thermal CO Oxidation and Photocatalytic CO2 Reduction over Bare and M-Al2O3 (M = Co, Ni, Cu, Rh, Pd, Ag, Ir, Pt, and Au) Cotton-Like Nanosheets

Aluminum oxide (Al2O3) has abundantly been used as a catalyst, and its catalytic activity has been tailored by loading transition metals. Herein, γ-Al2O3 nanosheets were prepared by the solvothermal method, and transition metals (M = Co, Ni, Cu, Rh, Pd, Ag, Ir, Pt, and Au) were loaded onto the nanosheets. Big data sets of thermal CO oxidation and photocatalytic CO2 reduction activities were fully examined for the transition metal-loaded Al2O3 nanosheets. Their physicochemical properties were examined by scanning electron microscopy, high-resolution transmission electron microscopy, X-ray diffraction crystallography, and X-ray photoelectron spectroscopy. It was found that Rh, Pd, Ir, and Pt-loading showed a great enhancement in CO oxidation activity while other metals negated the activity of bare Al2O3 nanosheets. Rh-Al2O3 showed the lowest CO oxidation onset temperature of 172 °C, 201 °C lower than that of bare γ-Al2O3. CO2 reduction experiments were also performed to show that CO, CH3OH, and CH4 were common products. Ag-Al2O3 nanosheets showed the highest performances with yields of 237.3 ppm for CO, 36.3 ppm for CH3OH, and 30.9 ppm for CH4, 2.2×, 1.2×, and 1.6× enhancements, respectively, compared with those for bare Al2O3. Hydrogen production was found to be maximized to 20.7 ppm during CO2 reduction for Rh-loaded Al2O3. The present unique pre-screening test results provided very useful information for the selection of transition metals on Al2O3-based energy and environmental catalysts.