Comprehensive experimental investigation of the effective parameters on stability of silica nanoparticles during low salinity water flooding with minimum scale deposition into sandstone reservoirs

Recent studies showed the high potential of nanofluids as an enhanced oil recovery (EOR) agent in oil reservoirs. This study aimed to investigate the effects of salts and ions, the salinity of aqueous solution, total dissolved solids (TDS), scale deposition of mixing brines, surface charge as zeta potential (ZP) value, and pH of injected brines as low salinity water (LSW) on the stability of silica nanoparticles (NPs). The experiments were conducted on the stability of silica NPs at different concentrations and brines to determine optimum salinity, dilution, cations, and anions concentrations. The results showed that 10 times diluted seawater (SW#10D) was optimum low salinity water (OLSW) as injected LSW and water-based nanofluids. Results showed that by decreasing the salinity, increasing seawater dilution, and removing Mg 2+ and Ca 2+ cations, the amount of scale deposition decreased, and the brine's brine's brine stability of NPs in brine improved. At the optimum salinity and dilution conditions, compared with other salinities, there was less scale formation with more nanofluid stability. Obtained results from ZP measurements and dynamic light scattering (DLS) showed that by removing divalent ions (Mg 2+ and Ca 2+ ) of water-based nanofluid (low salinity hard water (LSHW) composition), more NPs were attached to the surface due to the reduction in repulsive forces between the NPs. Therefore, at optimum low salinity soft water (OLSSW), more wettability alteration occurred compared with optimum low salinity hard water (OLSHW) due to the more stability of NPs in OLSSW. The obtained results from the contact angle measurements, surface adsorption of the NPs by FESEM images, and ZP measurements showed that the predominant mechanism in enhancing oil recovery by nanofluid was the wettability alteration by disjoining pressure. According to wettability alteration results, the silica NPs with an optimized concentration in the optimized LSHW and LSSW compositions could be improved the wettability alteration by up to 23.37% and 55.81% compared with the without NPs. The optimized LSSW compared with LSHW composition could be improved the wettability alteration by up to 11.69%. In addition, OLSSW-based nanofluid compared with OLSHW could be increased wettability alteration toward strongly water-wet by up to 33.44%.