Diamond-structured nanonetwork gold as mechanical metamaterials from bottom-up approach

Herein, this work aims to develop a facile method for the fabrication of metallic mechanical metamaterial with a well-ordered diamond structure from a bottom-up approach using a self-assembled block copolymer for templated electrochemical deposition. By controlling the effective volume fraction of PDMS in PS- b -PDMS via solvent annealing followed by HF etching of PDMS, it is feasible to obtain nanoporous PS with diamond-structured nanochannels and used it as a template for templated electrochemical deposition. Subsequently, well-ordered nanonetwork gold (Au) can be fabricated. As evidenced by nanoindentation and micro-compression tests, the mechanical properties of the diamond-structured Au after removal of PS give the combination of lightweight and mechanically robust characteristics with an exceptionally high reduced elastic modulus of 11.9 ± 0.6 GPa and yield strength of 193 ± 11 MPa above the Hashin-Shtrikman upper bound of 72 MPa with a bending-dominated structure at equivalent density. The corresponding deformation mechanism can be elucidated by morphological observations experimentally and finite element analysis (FEA) numerically. This work demonstrates the bottom-up approach to fabricating metallic monolith with diamond structure in the nanoscale, giving a superior performance as mechanical metamaterials. This work aims to fabricate well-ordered nanonetwork Au through a bottom-up approach using templated electrochemical deposition for enhanced mechanical properties. As evidenced by nanoindentation and micro-compression tests, diamond-structured Au fabricated exhibits high reduced modulus and yield strength above the Hashin-Shtrikman upper bound due to the deliberate structuring and nanosized effects.