Effect of oxygen contents on strain rate sensitivity of commercially pure titanium

In this study, we have investigated the effect of oxygen contents on strain rate senstivitiy (SRS) within Gr. 1 and 4 commercially pure titanium (CP-Ti). The SRS was evaluated in multi-scales using macro-scopic tensile test with constant strain rate (CSR) method and strain rate jump (SRJ) method, an...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:MATEC Web of Conferences 2020, Vol.321, p.4009
Hauptverfasser: Lee, Min-Su, Hyun, Yong-Taek, Jun, Tea-Sung
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this study, we have investigated the effect of oxygen contents on strain rate senstivitiy (SRS) within Gr. 1 and 4 commercially pure titanium (CP-Ti). The SRS was evaluated in multi-scales using macro-scopic tensile test with constant strain rate (CSR) method and strain rate jump (SRJ) method, and nanoindentation test with SRJ method. Electron backscatter diffraction (EBSD) has been used to characterise crystallographic texture and individual grain orientation of samples. Slip and twin activities of each CP-Ti were compared by EBSD measurements and the associated Schmid factor (SF) analysis. The active slip system is anticipated to be different in each relation between loading directions and textures, but twin activity is much similar. The texture dependent global SRS is thus thought to be resulted from the different slip activity. Local SRS was dependent not only on the grain orientation but also on the oxygen contents, leading to the fact that the impact of oxygen contents is closely correlated in macro- and micro-scopic level.
ISSN:2261-236X
2274-7214
2261-236X
DOI:10.1051/matecconf/202032104009