Synthesis and PL study of Sr3 (VO4 ) 2 :Eu3+ phosphor for W-LED application

In the present paper, a single host phosphor for a white light emitting diode (W-LED) Sr3(VO4)2:Eu3+, prepared by the co-precipitation method and combustion one, has been reported. Formation of the compound was confirmed by studying the X-ray diffraction pattern. The photoluminescence (PL) properties were studied by fluorescence spectrophotometer F-7000. The Sr3(VO4)2:Eu3+ exhibited a broad emission band covering the entire visible region centered at 520 nm wavelength and a sharp peak at 613 nm, when excited by 350 nm. The excitation spectrum at 520 nm emission wavelength was found to be suitable for pc-W-LED application. В статье исследован люминофор Sr3(VO4)2:Eu3+, перспективный для создания белого светоизлучающего диода (W-LED) на основе этого одного соединения. Образцы данного материала были получены двумя способами: соосаждения и сжигания. Образование требуемого вещества было подтверждено рентгенографически. Практически важные свойства объекта изучались методом фотолюминесцентной спектроскопии. В спектрах соединения обнаружены широкая эмиссионная полоса, охватывающая всю видимую область спектра с центром на длине волны 520 нм, а также острый пик на 613 нм. В спектрах возбуждения люминесценции наблюдалась широкая полоса с центром на длине волны 350 нм. Представлена соответствующая диаграмма энергетических уровней. Полученные экспериментальные результаты привели к заключению, что метод соосаждения предпочтителен, а фотолюминесцентные свойства полученного люминофора удобны для создания штучных белых светоизлучающих диодов.