Comparison of Wear Resistance of Hawley and Vacuum Formed Retainers: An in-vitro Study

As a physical property, wear resistance of the materials used in the fabrication of orthodontic retainers play a significant role in the stability and long term use of the appliances. To evaluate the wear resistance of two commonly used materials for orthodontic retainers: Acropars OP, i.e. a polymethyl methacrylate based material, and 3A-GS060, i.e. a polyethylene based material. For each material, 30 orthodontic retainers were made according to the manufacturers' instructions and a 30×30×2 mm block was cut out from the mid- palatal area of each retainer. Each specimen underwent 1000 cycles of wear stimulation in a pin on disc machine. The depth of wear of each specimen was measured using a Nano Wizard II atomic force microscope in 3 random points of each specimen's wear trough. The average of these three measurements was calculated and considered as mean value wear depth of each specimen (µm). The mean wear depth was 6.10µm and 2.15µm for 3A-GS060 and Acropars OP groups respectively. Independent t-test showed a significant difference between the two groups ( < 0.001). The results show Polymethyl methacrylate base (Acropars) is more wear resistance than the polyethylene based material (3A-GS060). As the higher wear resistance of the fabrication material can improve the retainers' survival time and its cost-effectiveness, VFRs should be avoided in situations that the appliance needs high wear resistance such as bite blocks opposing occlusal forces.