Hot deformation behavior and microstructure evolution model of 7055 aluminum alloy

Hot compression tests were conducted on 7055 aluminum alloy under different strain rates, temperatures, and reduction ratios. The influence of deformation parameters on microstructure evolution and hot deformation behavior was studied through EBSD and TEM characterization. An Arrhenius constitutive...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials research and technology 2023-11, Vol.27, p.3191-3213
Hauptverfasser: Liu, Linlin, Zhao, Guoqun, Wang, Guangchun, Ma, Xinwu, Yan, Zhaohui, Cao, Shanpeng
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Hot compression tests were conducted on 7055 aluminum alloy under different strain rates, temperatures, and reduction ratios. The influence of deformation parameters on microstructure evolution and hot deformation behavior was studied through EBSD and TEM characterization. An Arrhenius constitutive model was established and the recovery and recrystallization characteristics of the alloy under different conditions were analyzed. Results showed that the softening mechanism during the hot compression process of 7055 aluminum alloy was mainly attributed to recovery and partial recrystallization. The Zener-Holloman (Z) parameter was utilized to reveal the combined effects of strain rate and temperature on recrystallization behavior. Under conditions of high LnZ values (20 
ISSN:2238-7854
DOI:10.1016/j.jmrt.2023.10.165