Optimization of Yb:CaF2 Transparent Ceramics by Air Pre-Sintering and Hot Isostatic Pressing
Yb:CaF2 transparent ceramics represent a promising laser gain medium for ultra-short lasers due to their characteristics: low phonon energy, relatively high thermal conductivity, negative thermo-optical coefficient, and low refractive index. Compared to single crystals, Yb:CaF2 ceramics offer superi...
Gespeichert in:
Veröffentlicht in: | Ceramics 2024-09, Vol.7 (3), p.1053-1065 |
---|---|
Hauptverfasser: | , , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Yb:CaF2 transparent ceramics represent a promising laser gain medium for ultra-short lasers due to their characteristics: low phonon energy, relatively high thermal conductivity, negative thermo-optical coefficient, and low refractive index. Compared to single crystals, Yb:CaF2 ceramics offer superior mechanical properties, lower cost, and it is easier to obtain large-sized samples with proper shape and uniform Yb3+ doping at high concentrations. The combination of air pre-sintering and Hot Isostatic Pressing (HIP) emerges as a viable strategy for achieving high optical quality and fine-grained structure of ceramics at lower sintering temperatures. The properties of the powders used in ceramic fabrication critically influence both optical quality and laser performance of Yb:CaF2 ceramics. In this study, the 5 atomic percentage (at.%) Yb:CaF2 transparent ceramics were fabricated by air pre-sintering and hot isostatic pressing (HIP) using nano-powders synthesized through the co-precipitation method. The co-precipitated powders were optimized by studying air calcination temperature (from 350 to 550 °C). The influence of calcination temperature on the microstructure and laser performance of Yb:CaF2 ceramics was studied in detail. The 5 at.% Yb:CaF2 transparent ceramics air pre-sintered at 625 °C from powders air calcined at 400 °C and HIP post-treated at 600 °C exhibited the highest in-line transmittance of 91.5% at 1200 nm (3.0 mm thickness) and the best laser performance. Specifically, a maximum output power of 0.47 W with a maximum slope efficiency of 9.2% at 1029 nm under quasi-CW (QCW) pumping was measured. |
---|---|
ISSN: | 2571-6131 |
DOI: | 10.3390/ceramics7030069 |