Processing and Properties of Fire Resistant EPDM Rubber-Based Ceramifiable Composites

Low softening point temperature glassy frit, reinforcing silica, wollastonite and dicumyl peroxide were incorporated into ethylene-propylene-diene (EPDM) rubber matrix in different amounts in order to obtain ceramifiable composites. Kinetics of vulcanization of the mixes was measured. Mechanical properties, micromorphology, thermal properties and combustibility of the vulcanizates were studied as well as compression strength of the ceramic residue obtained after heat treatment. Studies show that optimal amount of glassy frit from the point of view of ceramification effectiveness in dispersed mineral phase is 40 % wt.