Nickel Hydroxide Nanofluid Cathodes with High Solid Loadings and Low Viscosity for Energy Storage Applications

Nanofluid electrodes with high loading of active solid materials have significant potential as high energy density flow battery electrolytes; however, two key criteria need to be met: they must have a manageable viscosity for pumping and simultaneously exhibit good electrochemical activity. A typical dispersion of nickel hydroxide nanoparticles (~100 nm) is limited to 5–10 wt.% of solids, above which it has a paste-like consistency, incompatible with flow applications. We report on the successful formulation of stable dispersions of a nano-scale nickel hydroxide cathode (β-Ni(OH)2) with up to 60 wt.% of solids and low viscosity (32 cP at 25 °C), utilizing a surface graft of small organic molecules. The fraction of grafting moiety is less than 3 wt.% of the nanoparticle weight, and its presence is crucial for the colloidal stability and low viscosity of suspensions. Electrochemical testing of the pristine and modified β-Ni(OH)2 nanoparticles in the form of solid casted electrodes were found to be comparable with the latter exhibiting a maximum discharge capacity of ~237 mAh/g over 50 consecutive charge–discharge cycles, close to the theoretical capacity of 289 mAh/g.