Enhancing the Antibacterial Properties and Biocompatibility of Ti-Cu Alloy by Roughening and Anodic Oxidation

Although Ti-Cu alloys have been shown to possess good antibacterial properties, they are still biologically inert. In this study, sandblasting and acid etching combined with anodic oxidation were applied to roughen the surface as well as to form a TiO2/CuO/Cu2O composite film, which would benefit both the antibacterial properties and the biocompatibility. The surface morphology, the phase composition, and the physicochemical properties were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Electrochemical testing and inductively coupled plasma spectrometry (ICP) were used to determine the corrosion resistance and Cu ion release, the plate counting method was used to evaluate the antibacterial performance, and the CCK-8 method was used to evaluate the cytocompatibility. It was revealed that a rough surface with densely porous double layer composed of TiO2/CuO/Cu2O was produced on Ti-Cu alloy surface after the combined surface modification, which enhanced the corrosion resistance significantly. The plate counting results demonstrated that the modified sample had strong long-term antibacterial performance (antibacterial rate > 99%), which was attributed to the formation of TiO2/CuO/Cu2O composite film. The cell compatibility evaluation results indicated that the surface modification improved the cytocompatibility. It was demonstrated that the combined modification provided very strong antibacterial ability and good cytocompatiblity, potentially making it a good candidate surface modification technique for Ti-Cu alloy for biomedical applications.