Study of Radiation Embitterment and Degradation Processes of Li2ZrO3 Ceramic under Irradiation with Swift Heavy Ions

The work is devoted to the study of radiation damage and subsequent swelling processes of the surface layer of Li2ZrO3 ceramics under irradiation with heavy Xe22+ ions, depending on the accumulation of the radiation dose. The samples under study were obtained using a mechanochemical synthesis method. The samples were irradiated with heavy Xe22+ ions with an energy of 230 MeV at irradiation fluences of 1011–1016 ion/cm2. The choice of ion types is due to the possibility of simulating the radiation damage accumulation processes as a result of the implantation of Xe22+ ions and subsequent atomic displacements. It was found that, at irradiation doses above 5 × 1014 ion/cm2, point defects accumulate, which leads to a disordering of the surface layer and a subsequent decrease in the strength and hardness of ceramics. At the same time, the main process influencing the decrease in resistance to radiation damage is the crystal structure swelling as a result of the accumulation of defects and disordering of the crystal lattice.