Application of Coating Mixture Based on Silica Aerogel to Improve Thermal Protective Performance of Fabrics

The main aim of this research is to improve the protective thermal performance of fabrics. Flame-resistant fabrics characterizing comparable thermal properties were chosen, cotton fabric with a flame-retardant finish and Nomex fabric. To improve thermal parameters the coating mixture, based on silica aerogel, was applied on one side of the sample surface. Parameters such as the thermal conductivity, resistance to contact, and radiant heat were determined based on the standards, which set high expectations for the protective clothing. Analysis of the coated fabrics surfaces was conducted based on confocal microscopy. It was found that the coating mixture caused a decrease in thermal conductivity. All the modified fabrics reached 1st efficiency level of protection against contact and radiant heat. The best sample from the point of view of protection against contact and radiant heat was modified cotton fabric with a flame-retardant finish. The coating mixture contained 45 wt% of silica aerogel. Moreover, better adhesion of the coating mixture to the cotton fabric compared with Nomex fabric was observed.