Thermo‐Responsive Ultrafiltration Block Copolymer Membranes Based on Polystyrene‐block‐poly(diethyl acrylamide)
Within the present work, a thermo‐responsive ultrafiltration membrane is manufactured based on a polystyrene‐block‐poly(diethyl acrylamide) block copolymer (BCP). The poly(diethyl acrylamide) block segment features a lower critical solution temperature (LCST) in water, similar to the well‐known poly...
Gespeichert in:
Veröffentlicht in: | Macromolecular materials and engineering 2023-11, Vol.308 (11), p.n/a |
---|---|
Hauptverfasser: | , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Within the present work, a thermo‐responsive ultrafiltration membrane is manufactured based on a polystyrene‐block‐poly(diethyl acrylamide) block copolymer (BCP). The poly(diethyl acrylamide) block segment features a lower critical solution temperature (LCST) in water, similar to the well‐known poly(N‐isopropylacrylamide), but having increased biocompatibility and without exhibiting a hysteresis of the thermally induced switching behavior. The BCP is synthesized via sequential “living” anionic polymerization protocols and analyzed by 1H‐NMR spectroscopy, size exclusion chromatography, and differential scanning calorimetry. The resulting morphology in the bulk state is investigated by transmission electron microscopy (TEM) and small‐angle X‐ray scattering (SAXS) revealing the intended hexagonal cylindrical morphology. The BCPs form micelles in a binary mixture of tetrahydrofuran and dimethylformamide, where BCP composition and solvent affinities are discussed in light of the expected structure of these micelles and the resulting BCP membrane formation. The membranes are manufactured using the non‐solvent induced phase separation (NIPS) process and are characterized via scanning electron microscopy (SEM) and water permeation measurements. The latter are carried out at room temperature and at 50 °C revealing up to a 23‐fold increase of the permeance, when crossing the LCST of the poly(diethyl acrylamide) block segment in water.
A novel ultrafiltration membrane based on a polystyrene‐b‐poly(diethyl acrylamide) block copolymer is introduced, where the poly(diethyl acrylamide) block features an lower critical solution temperature in water at 32 °C. The membrane is fabricated via the non‐solvent induced phase separation process and the reversible thermal switching capability of water permeance is shown. |
---|---|