The Deformation Behavior of Oxygen-Modified Ti-29Nb-13Ta-4.6Zr(wt.%)

A series of Ti-29Nb-13Ta-4.6Zr(wt.%) {TNTZ} alloys containing either 0.1, 0.3 or 0.7(wt.%) oxygen (O) were room-temperature tensile tested inside a scanning electron microscope to evaluate the effect of O on the deformation evolution. The deformation modes observed for TNTZ-0.1O, which exhibited the...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:MATEC web of conferences 2020, Vol.321, p.11003
Hauptverfasser: Khademi, V., Liu, H., Nakai, M., Niinomi, M., Boehlert, C.J.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:A series of Ti-29Nb-13Ta-4.6Zr(wt.%) {TNTZ} alloys containing either 0.1, 0.3 or 0.7(wt.%) oxygen (O) were room-temperature tensile tested inside a scanning electron microscope to evaluate the effect of O on the deformation evolution. The deformation modes observed for TNTZ-0.1O, which exhibited the largest elongation-to-failure and lowest strength of all the alloys, were deformation-induced α”-martensitic transformation, {332} twinning, and slip. For the other two alloys, slip was the dominant deformation mode, where TNTZ-0.7O exhibited more homogeneous and extensive slip, a higher frequency of cross slip, and a higher work-hardening rate, all of which contributed to both its strength and elongation-to-failure being greater than that for TNTZ-0.3O. TNTZ-0.3O exhibited the greatest tendency for cracking, which generally occurred on grain boundaries perpendicular to the tensile axis, leading to the lowest elongation-to-failure of all the alloys.
ISSN:2261-236X
2274-7214
2261-236X
DOI:10.1051/matecconf/202032111003