Wear Analysis of Plasma Sprayed Calcium and Strontium Zirconates on Inconel 718
CaZrO3and SrZrO3powders were prepared by sol-gel synthesis and plasma sprayed over the Inconel 718 substrate,forming a wear-resistant ceramic coating. X-Ray Diffraction (XRD) analysis of synthesized ceramic powders revealed the presence of CaZrO3and SrZrO3 phases, having an orthorhombic structure. C...
Gespeichert in:
Veröffentlicht in: | Materials research (São Carlos, São Paulo, Brazil) São Paulo, Brazil), 2024-01, Vol.27, p.1 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | CaZrO3and SrZrO3powders were prepared by sol-gel synthesis and plasma sprayed over the Inconel 718 substrate,forming a wear-resistant ceramic coating. X-Ray Diffraction (XRD) analysis of synthesized ceramic powders revealed the presence of CaZrO3and SrZrO3 phases, having an orthorhombic structure. CaZrO3 and SrZrO3powders were sprayed onto the surface of Inconel 718using a plasma spraying process. Scanning Electron Microscope (SEM)analysis of CaZrO3and SrZrO3coated samplesshowedanaveragethickness of about 400μm.Wear depth and wear mechanism for the above sampleswerestudiedusing Pin-on-disc apparatus. Wear results of CaZrO3 and SrZrO3 coated substrates revealed that high wear depths were observed at high speeds and loads. SEM investigations of wornout samples revealed that both CaZrO3 and SrZrO3 coated samples had undergone delamination wear. CaZrO3 coated samples had exhibitedless delamination and wear depth than SrZrO3 coated samples, thus showing relatively better wear resistance. |
---|---|
ISSN: | 1516-1439 1980-5373 1980-5373 |
DOI: | 10.1590/1980-5373-MR-2022-0282 |