Temperature effect on photovoltaic modules power drop

In order to determine what type of photovoltaic solar module could best be used in a thermoelectric photovoltaic power generation. Changing in powers due to higher temperatures (25oC, 35oC, and 45oC) have been done for three types of solar modules : monocrystalline, polycrystalline, and copper indium gallium (di) selenide (CIGS). The Prova 200 solar panel analyzer is used for the professional testing of three solar modules at different ambient temperatures ; 25oC, 35oC, and 45oC and solar radiation range 100-1000 W/m2. Copper indium gallium (di) selenide module has the lowest power drop (with the average percentage power drop 0.38 % /oC) while monocrystalline module has the highest power drop (with the average percentage power drop 0.54 % /oC), while polycrystalline module has a percentage power drop of 0.49 % /oC. من أجل تحديد أي نوع من وحدات الخلايا الشمسية يكون استخدامها أفضل مع زيادة درجة الحرارة. تغير القدرة نتيجة زيادة درجات الحرارة (25o C, 35o C, and 45o C) تم إيجاده لثلاث أنواع من وحدات الخلايا الشمسية و هي أحادية التبلور، ثنائية التبلور، و نحاس – أنديوم – جليوم و السليناد الثنائي. لقد استعمل جهاز بروفا 200 لتحليل الخلايا الشمسية لفحص وحدات الخلايا الشمسية الثلاث و في درجات حرارة مختلفة : 25، 35، و 45 درجة مئوية و ضمن مدى إشعاع شمسي 100 إلى 1000 واط لكل متر مربع. وحدة الخلية نوع نحاس – أنديوم – جليوم و السليناد الثنائي هي الأقل انخفاض في قدرة 0.38 % / oC بينما وحدة الخلية نوع أحادية التبلور هي الأعلى 0.54 % / oC. بينما وحدة الخلية متعددة التبلور كانت نسبة انخفاض الفولتية هي 0.49 % / oC.