Zro2 tetragonal obtenido po rel método de precipitación controlada

In this work, ZrO2 tetragonal stabilized with calcium oxide was synthesized by the controlled precipitation method. Ceramics powders were characterized using Differential Thermal Analysis and Thermal Gravimetry Analysis, (DTA/TG), Fourier Transform Infrared Spectroscopy (FTIR), Xray diffraction (XRD) and Transmission Electron Microscopy (TEM). Results show that ceramic powders treatment thermally at 600 ºC, presents ZrO2 in tetragonal crystalline phase; this powder contained particles of nanometric size. The mechanism formation of particles was discussed En este trabajo se utilizó el método de precipitación controlada para sintetizar ZrO2 tetragonal estabilizado con óxido de calcio, CaO. Los sólidos obtenidos se caracterizaron utilizando análisis térmico diferencial y gravimétrico (ATD/TG), Espectroscopia Infrarroja con transformada rápida de Fourier (FTIR), Difracción de Rayos X (DRX), y microscopia electrónica de transmisión (MET). Los resultados indican que al tratar el polvo cerámico a una temperatura de 600 º C se obtiene ZrO2 con fase cristalina tetragonal; además las partículas de ZrO2 presentaron tamaño nanométrico (< 100 nm). Se prestó especial atención a los posibles mecanismos de formación de las partículas.