Endurecimiento por precipitación en aleaciones al-4%cu-0.5%mg modificadas con ag

The study of the precipitation hardening in the Al-4%Cu-0.5%Mg alloy with additions of 0.5-4%Ag was carried out by transmission electron microscopy (TEM) and hardness Vickers (HV) measurements. Alloys were homogenized at 525°C for 7 days and then quenched. The precipitation was induced by aging treatments at 150, 200 and 250°C for different times. The addition up to 3%Ag promotes an increase in hardness for all the treatments of aged. Additionally, the TEM results showed that the coexistence of the è' and Ù phases are responsible for the increase in hardness. On the other hand, the TEM analysis confirms that the Ù phase has an fcc structure, it is coherent with the á phase matrix, and its morphology is hexagonal with interfaces aligned in the [311]á, [022]á and [111]á. Finally, the decrease in hardness is attributed to the disappearance of the è' phase and the coarsening of the Ù phase. El estudio del endurecimiento por precipitacion en la aleacion Al-4%Cu- 0.5%Mg con adiciones de 0.5-4%Ag se realizo mediante microscopia electronica de transmision (MET) y microdureza Vickers. Las aleaciones fueron homogeneizadas a 525 C durante 7 dias y templadas. Los tratamientos de precipitacion se realizaron a 150, 200 y 250 C por diferentes tiempos. La adicion de hasta 3%Ag promueve un aumento en dureza para todos los tratamientos de envejecido. Adicionalmente, los resultados muestran que la coexistencia de las fases Æ f y ¶ son las responsables de promover el aumento en dureza. Por otra parte, los analisis de MET confirman que la fase ¶ tiene una estructura fcc, es coherente con la matriz, y su morfologia es hexagonal con intercaras alineadas en las direcciones [311] ¿, [022] ¿ y [111] ¿. Finalmente, la disminucion en la dureza de las aleaciones se atribuye a la desaparicion de la fase Æ f y al engrosamiento de la fase ¶.