Estudio del desgaste erosivo por cavitación a nivel del tipo de límites y orientación cristalina de los granos en un acero inoxidable austenítico de alto nitrógeno

The effect of the type of grain boundaries and crystalline orientation on cavitation erosion wear (E-C) in an austenitic stainless steel with 0.9 % N2 was studied. A 100% austenitic structure was obtained by high temperature gas nitriding of a UNS S31803 duplex stainless steel. The samples were submitted to cavitation-erosion tests in a vibratory apparatus using distilled water during 64 h. Tests were periodically interrupted for analyzing the mass loss and surface damage using Scanning Electron Microscopy SEM. The type of grain boundaries were determined by electron back-scattering diffraction (EBSD). It was observed that grain boundaries, known as Twins ( CSL 4-3), presented the worst behavior on E-C and the grains with (101)//surface orientation presented the best behavior on E-C En este trabajo se estudió el efecto que tiene el tipo de límites y la orientación cristalina de los granos, sobre la resistencia al desgaste erosivo por cavitación (E-C), en un acero inoxidable austenítico con 0,9% en peso de nitrógeno,. Este acero fue obtenido a partir de la nitruración gaseosa en alta temperatura de un acero inoxidable duplex UNS S31803. Las muestras fueron ensayadas a cavitación vibratoria en agua destilada durante 64 h. Los ensaios fueron periodicamente interrumpidos para medir la pérdida de masa y hacer el seguimiento del daño superficial de las muestras con ayuda de un microscopio electrónico de barrido (MEB). El tipo de límites de grano fue obtenido por medio de la técnica de difracción de electrones retro-proyectados (EBSD). Los resultados mostraron que el tipo de límites de grano, conocidos como maclas (CSL >-3), tiene el peor comportamieto frente a la E-C, y que el tipo de granos con orientación cristalina (101), presenta el mejor comportamiento frente a este tipo de desgaste.