Effects of 1-Ethyl-3-(3-Dimethylaminopropyl) Carbodiimide on Adhesion of Posts in Teeth Obturated With Different Sealers

Abstract The aim of this study was to evaluate the effect of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) on bond strength of fiberglass posts in root canals obturated with different endodontic sealers. Seventy-eight mandibular premolars were obturated with three sealers (n=26): Endofill (END), AH Plus (AHP), and Endosequence BC Sealer (EBS). After preparation of the post space, two subgroups were formed according to the cementation of the posts (n=13): with EDC (EDC), and without EDC (control - CON). The specimens were submitted to a pull-out test, failure mode classification, and root canal surface evaluation by scanning electron microscopy after post displacement. Regarding the bond strength, a significant difference between the EDC and CON subgroups occurred only in the END (p=0.001). No difference was detected among the CON subgroups (p=0.339). However, among the EDC subgroups, AHP presented significantly higher values (END versus AHP: p=0.001; AHP versus EBS: p=0.016). Upon classification of failure modes, score 1 (≥ 50% of cement) was the most commonly observed, except for the END + EDC. Remains of endodontic sealers and resin cements were found in the cervical third, but without statistical difference (p=0.269), while in the middle third, difference occurred (p=0.004). In conclusion, EDC decreases bond strength when associated with END sealer, without changing the failure mode between the resin cement and fiberglass post. The best performance was observed when EDC was combined with AHP sealer.