The Application of Borosiloxane to Strengthening of Carbon Fiber/Ceramic Composites
Carbon fiber/ceramic composites (CFRC) were prepared from carbon fiber (CF) and organometallic compound (diphenylborosiloxane). The CF cloth laminates impregnated with diphenylborosiloxane containing SiC micropowder (4μm in size), were heated at 500°C in air, and reheated at 1000°C in N2. Then densi...
Gespeichert in:
Veröffentlicht in: | TANSO 1991/04/15, Vol.1991(147), pp.74-79 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Carbon fiber/ceramic composites (CFRC) were prepared from carbon fiber (CF) and organometallic compound (diphenylborosiloxane). The CF cloth laminates impregnated with diphenylborosiloxane containing SiC micropowder (4μm in size), were heated at 500°C in air, and reheated at 1000°C in N2. Then densification was carried out on the CF cloth laminates to increase thier density and strength. Thus prepared CFRC plates (2mm in thickness) showed a bulk density of 1.22g/cm3 and a bending strength of 43MPa. The bending strength (59MPa) of CFRC plate prepared with a high temperature hot press, was higher than 1.4 times than CFRC without it. The mechanical properties of CFRC were influenced by the temperature of pressure application. |
---|---|
ISSN: | 0371-5345 1884-5495 |
DOI: | 10.7209/tanso.1991.74 |