The Dispersion Tolerance of Micro/Nano Particle in Polydimethylsiloxane and Its Influence on the Properties of Fouling Release Coatings Based on Polydimethylsiloxane

Particles can be used to improve the mechanical properties of fouling release coatings based on polydimethylsiloxane (PDMS). In this study, coatings were prepared by high speed stirring using seven types of particles, with different particle size from nanometer to micrometer. The influence of specific surface area of the particles on the dispersion tolerance was investigated. The results showed that the dispersion tolerance of particles in PDMS decreased with the increase in specific surface area of the particle, and for nano particles, the factor most affecting the dispersion tolerance was the specific surface area of agglomerate particle. Subsequently, the surface properties, mechanical properties, and biofilm adhesion assay of coatings were investigated. Results indicated that surface roughness increased with the increase of dispersion tolerance. Surface roughness of samples improved the hydrophobicity of samples, yet the polar chemical group of nano silica and fumed silica reduced the hydrophobicity of samples. Further, particles could enhance the mechanical properties of coating, especially nano particles. Compared to the coating without particle, biofilm adhesion performance of coating with particles decreased, which was determined by the increase of the elastic modulus and surface roughness of coatings.