Synthesis and characterization of NbCr 2 Laves phase produced by spark plasma sintering

The NbCr 2 Laves phase was fabricated by spark plasma sintering (SPS) using spherical Nb and Cr powders. The experimental results revealed that increasing the sintering temperature to 1773 K can result in the formation of NbCr 2 Laves phase as major phase, but it always appeared with trace amounts of Nb and Cr solid solutions. Based on the theoretical calculations, the residual of Nb and Cr solid solutions was attributed to the inhomogeneous distribution of temperature increase from the particle-contacting surface to the center of particle when pulsed current passed through. Moreover, the hardness and fracture toughness of the SPS-processed NbCr 2 attained 14.05 ± 0.67 GPa and 8.9 MPa·m 1/2 , which were 1.6 and 7.4 times of the as-cast NbCr 2 Laves phase (1.2 MPa·m 1/2 ). The formation of ductile Nb and Cr solid solutions and fine grains were considered to be the reason for the remarkable enhancements in mechanical properties.