Microindentation and nanoindentation of human fingernails at varying relative humidity

The indentation properties of human fingernails at varying humidity are reported. The samples were indented using both microindentation, to obtain their Vickers hardness and also nanoindented using a Berkovich indenter tip. The relative humidity (RH) of the samples was controlled by using salt solut...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials research 2009-03, Vol.24 (3), p.980-984
Hauptverfasser: Farran, Laura, Ennos, A. Roland, Eichhorn, Stephen J.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The indentation properties of human fingernails at varying humidity are reported. The samples were indented using both microindentation, to obtain their Vickers hardness and also nanoindented using a Berkovich indenter tip. The relative humidity (RH) of the samples was controlled by using salt solutions with a sealed and enclosed environment surrounding the testing equipment. It was shown that the Vickers hardness of the samples is sensitive to RH, with recovery of the nail material more readily occurring for nails tested at >55% RH. This recovery mechanism is discussed in terms of the structure of the nails, and this approach is also suggested as a technique for following recovery mechanisms in natural materials under varying humidity. The hardness obtained by nanoindentation is similar to previously published data, but does not change with humidity. The modulus of the nails is also insensitive to relative humidity, but in the same range as the value derived from the microindentation tests.
ISSN:0884-2914
2044-5326
DOI:10.1557/jmr.2009.0119